1.4542 (X5CrNiCuNb16-4) Material Data Sheet

Back to category page

1.4542 (X5CrNiCuNb16-4) directly from stock & cut to your required dimensions

International identifiers
AISI 630, AFNOR Z7CNU15-05, ASTM 17-4PH, UNS S17400, AFNOR Z7CNU17-04, JIS SUS630, GB 05Cr17Ni4Cu4Nb
Scopes

1.4542 is a stainless steel that exhibits good corrosion resistance, high yield strength and high wear resistance. It is analytically similar to 1.4548 and 17-4PH.

When stored at conditions H1150 and H1025, 1.4542 can also be worked at low temperatures! 1.4542 features excellent notch impact strength at minus temperatures.

1.4542 steel is suitable for use in maritime environments due to its combination of good mechanical properties and corrosion resistance.

1.4542 provides an excellent solution if stronger corrosion resistance and mechanical properties are required than those provided by martensitic steels.

This stainless steel is susceptible to crevice corrosion in stagnant seawater.

1.4542 is popularly known as AISI 630​​​​​.
 

Plant engineering, chemical industry, wood industry, offshore, shipbuilding, mechanical engineering, petroleum industry, paper industry, aerospace industry, sports and leisure industry.

1.4542 Material Data Sheet Download

Characteristics

solution annealed & quenched and aged

Weldability:       good

Machinability:   3 (1 = poor - 10 = good)

Polishability:          yes

Corrosion class:   3 (0 = poor - 5 = good)

 

Calculate the weight of the required material quickly »

Chemical composition
1.4542
X5CrNiCuNb16-4
CSiMnPSCrMoNiV
min.bis bisbisbisbis15,0bis3,0   
max.0,070,71,00,0250,01517,00,65,0   
1.4542
X5CrNiCuNb16-4
AlCuNNbTiSonstiges
min.   3,0   5xC    
max.   5,0    0,45    
In stock

flat, forged, solution annealed & quenched and aged

Stahlblock
Advantages of saw cut

The processing with the saw is a mechanical processing of the material, which results in a significantly lower unintended deformation and increased hardness for the existing structure, such as the thermal cutting.

Thus, the machined workpiece has a homogeneous structure even at the edge, which does not change in the continuation of the material.
This circumstance allows immediate finishing of the workpiece with milling or drilling . So it is not necessary to anneal the material or make a similar operation beforehand.

The most important questions and answers about the material 1.4542:

Wie ist die Korrosionsbeständigkeit von 1.4542?

1.4542 ist ein korrosionsbeständiger Werkstoff, kann jedoch unter bestimmten Umgebungseinflüssen auch rosten.

Ist 1.4542 magnetisch?

Ja, 1.4542 ist ein ferromagnetischer Werkstoff.

Welche Härte hat 1.4542?

1.4542 kann eine große Bandbreite von Härtewerten erreichen, zwischen 255 HB bis über 400 HB. In der Kondition A Stufe soll eine Härte von 363HB nicht überschritten werden.

Welche Zugfestigkeit hat 1.4542?

Die Mindestzugfestigkeit des 1.4542 kann von 800 bis über 1300 MPa betragen.

Kann 1.4542 rosten?

1.4542 ist ein korrosionsbeständiger Werkstoff, kann jedoch unter bestimmten Umgebungseinflüssen auch rosten.

Wie ist die Wärmebehandlung von 1.4542?

1.4542 Stahl wird lösungsgeglüht bei Temperaturen um 1040°C, anschließend abgeschreckt und eventuell bei Temperaturen zwischen 480°C bis 760°C ausgelagert.

Do you have any questions?

We are happy to answer your questions and make you an offer for these and other materials. Contact us now for more information.

Antje Schroeder

Your contact person Antje Schroeder+49 (0) 35263-665-13

contact now

Notice: Specifications contained in following data sheet are provided as a description, liability is excluded!

 