1.4529 (X1NiCrMoCuN25-20-7) from stock

Back to category page

1.4529 sawn to your required size delivery directly from stock

International identifiers
Scopes

The material 1.4529 is a rustproof, super austenitic steel. It is resistant to organic and inorganic acids thanks to the alloy composition. In aggressive media there is good resistance to stress corrosion cracking and pitting.


Areas of application

The main areas of application for this super austenite are the construction industry, ship-building and use in sea and brackish water. In the chemical industry, for flue gas desulphurization plants, and in the medical industry.

 

Characteristics
Weldabilitygood
Machinability4 (1 = bad - 10 = good)
Polishingyes
Corrosion resistancegood
Malleabilitymedium
Mechanical propertiesgood

 

Welding: 1.4529 steel can be welded with all processes (TIG welding; MAG solid wire, ARC welding ). Because this material tends to form hot cracks, caution is advised! It is recommended to use a duplex filler material (for example: 1.4462) Link, which is characterized by good elongation properties. Nickel alloys are also suitable.
 

Forging: Before forging, the steel should be heated to 1150°C and 1180°C. The forging process takes place at 1180°C to 950°C with subsequent rapid air or water cooling.


Cold forming: Due to the high strain hardening, higher forming forces are required.
 

Corrosion resistance: The corrosion resistance is increased compared to conventional chrome-nickel-molybdenum steel and there is resistance to intergranular corrosion.
 

Machining: Machining is difficult due to the high alloy content. High-quality high-speed steel or hard metal should be used.


Heat treatment

The material must be free of impurities before heat treatment.

 TemperatureCooling
Hot forming1200°C - 950°CAir
   
Heat treatment  
Solution annealing (+ AT)1120°C - 1180°CWater, air (rapid cooling)

 

Processing:

Cold formingis possible
Cold upsettingis possible
Open die and drop forgingis possible
Machiningwith care possible
Automated machiningno

 

Special features:

  • Can be used in the temperature range up to 400°C

  • Easy to polish

  • Non-magnetic quality (μr <1.01)

Physical Properties:

Density (kg/dm3 )8,1
Electrical resistance at 20°C (Ω mm2 /m)1,0
Thermal conductivity at 20°C (W/m K)12
Specific heat capacity at 20°C (J/kg K)450
 Up to 160 mm WD
Tensile strength650 - 850 N/mm2 
Brinell hardness190 - 250 HB

 

Mechanical properties at room temperature: up to 160 mm

Rp0,2ARp1,0KV
N/mm2%N/mm2J
≥ 300≥ 40≥ 340≥ 100

 

Quick and easy to calculate the weight »

Chemical composition
1.4529CSiMnPSCrMoNi
min.     19,06,0024,00
max.0,0200,501,000,0300,01021,07,0026,00
1.4529VAlCuNNbTiW
min.  0,500,15   
max.  1,500,25   
In stock

Blech, gewalzt, lösungsgeglüht, abgeschreckt

Stahlblech
Advantages of saw cut

Das Gefüge des Materials zeigt eine deutlich geringere unbeabsichtigte Verformung und Materialaufhärtung durch die mechanische Bearbeitung mit der Bandsäge, als zum Beispiel durch das Brennschneiden. Somit verfügt das über die Säge bearbeitete Werkstück bereits an der Kante über ein homogenes Gefüge, das sich auch in der Fortsetzung des Materials nicht ändert. Dadurch wird das sofortige Endbearbeiten des Werkstücks mit Fräsen oder Bohren ermöglicht, ohne vorher ein Weichglühen oder ähnlichen Arbeitsschritt vornehmen zu müssen.

Do you have any questions?

We are happy to answer your questions and make you an offer for these and other materials. Contact us now for more information.

Alexandra Herbig

Your contact person Alexandra Herbig+49 (0) 35263-665-28

contact now

Notice: Specifications contained in following data sheet are provided as a description, liability is excluded!

 