1.2436 (X210CrW12) directly from stock & cut to your required dimensions!
![[Translate to Englisch:]](/fileadmin/user_upload/produkt-fotos/1.2436_Rundstahl_Block.jpg "[Translate to Englisch:]")
![[Translate to Englisch:]](/fileadmin/user_upload/produkt-fotos/1.2436_Rundstahl_Palette.jpg "[Translate to Englisch:]")
Ledeburitic 12% chromium steel, with wolfram addition (therefore better hardenability) highest wear resistance, good dimensional stability, high compressive strength, with a good toughness.
Roll- or table knives, drawing punch, straightening rolls, blanking dies in the paper- and plastic industry, molds in the ceramics industry, cold shear blades for thin sheets up to 2 mm thickness.
annealed max. 250 HB
Machinability: 3 (1 = very bad - 10 = good)
| 1.2436 X210CrW12 | C | Si | Mn | P | S | Cr | Mo | Ni | V |
|---|---|---|---|---|---|---|---|---|---|
| min. | 2,0 | 0,1 | 0,3 | 11,0 | |||||
| max. | 2,3 | 0,4 | 0,6 | 13,0 |
| 1.2436 X210CrW12 | Al | Cu | N | Nb | Ti | W |
|---|---|---|---|---|---|---|
| min. | 0,6 | |||||
| max. | 0,8 |
Round, forged, annealed
The processing with the saw is a mechanical processing of the material, which results in a significantly lower unintended deformation and increased hardness for the existing structure, such as the thermal cutting.
Thus, the machined workpiece has a homogeneous structure even at the edge, which does not change in the continuation of the material.
This circumstance allows immediate finishing of the workpiece with milling or drilling . So it is not necessary to anneal the material or make a similar operation beforehand.
Do you have any questions?
We are happy to answer your questions and make you an offer for these and other materials. Contact us now for more information.
Your contact person Andreas Blachowiak+49 (0) 35263-665-37blachowiak@stahlportal.com
Notice: Specifications contained in following data sheet are provided as a description, liability is excluded!